| spelling |
oapen-20.500.12657-492452021-11-23T13:49:23Z Chapter Self-healing of Structural Composites Containing Dendrimers as Healing Agent Kotrotsos, Athanasios Kostopoulos, Vassilis composites, self-healing, hydrogen bonds, supramolecular polymers, fracture mechanics, damage tolerance bic Book Industry Communication::P Mathematics & science::PH Physics::PHM Atomic & molecular physics Dendrimers exhibit healing functionalities on polymer level. In the present chapter, the effect of hydrogen-bonded supramolecular polymers (SP) into high performance aerospace carbon fiber reinforced plastics (CFRPs) is assessed. More precisely, the interlaminar fracture toughness of unidirectional (UD) SP-modified composites (containing SP interleaves) and their healing capability were measured under mode I and mode II fracture loading conditions. During testing, these modified samples exhibited extended bridging between the interlaminar crack flanks, which considerably enhanced their interlaminar fracture toughness. Furthermore, SP pre-impregnated fiber layers (prepregs) were fabricated to facilitate the introduction of the self-healing agent (SHA) into the composite laminated structure. SP prepregs were used to modify quasi-isotropic CFRPs in a symmetric fashion, and the damage tolerance of the modified composites was investigated. To that direction, the SP-modified laminates were tested under low velocity impact (LVI) conditions, and compression after impact (CAI) tests were conducted prior and after the activation of the healing. Finally, examination of the morphology of fracture surface led to qualitative conclusions regarding the involved failure and healing mechanisms. 2021-06-02T10:10:26Z 2021-06-02T10:10:26Z 2018 chapter ONIX_20210602_10.5772/intechopen.70884_359 https://library.oapen.org/handle/20.500.12657/49245 eng application/pdf n/a 57157.pdf InTechOpen 10.5772/intechopen.70884 10.5772/intechopen.70884 09f6769d-48ed-467d-b150-4cf2680656a1 FP7-AAT-2013-RTD-1 605412 open access
|
| description |
Dendrimers exhibit healing functionalities on polymer level. In the present chapter, the effect of hydrogen-bonded supramolecular polymers (SP) into high performance aerospace carbon fiber reinforced plastics (CFRPs) is assessed. More precisely, the interlaminar fracture toughness of unidirectional (UD) SP-modified composites (containing SP interleaves) and their healing capability were measured under mode I and mode II fracture loading conditions. During testing, these modified samples exhibited extended bridging between the interlaminar crack flanks, which considerably enhanced their interlaminar fracture toughness. Furthermore, SP pre-impregnated fiber layers (prepregs) were fabricated to facilitate the introduction of the self-healing agent (SHA) into the composite laminated structure. SP prepregs were used to modify quasi-isotropic CFRPs in a symmetric fashion, and the damage tolerance of the modified composites was investigated. To that direction, the SP-modified laminates were tested under low velocity impact (LVI) conditions, and compression after impact (CAI) tests were conducted prior and after the activation of the healing. Finally, examination of the morphology of fracture surface led to qualitative conclusions regarding the involved failure and healing mechanisms.
|